Performance of Geopolymer Concrete Exposed to
Freezing and Thawing Cycles
الباحث الأول:
Mohammed Shamsa
الباحثين الآخرين:
Asst. prof. Dr. Basil Al-Shathr
Prof. Dr. Tareq al-Attar
المجلة:
مجلة الهندسة والتكنولوجيا
تاريخ النشر:
None
مختصر البحث:
In this study, the effect of rapid freezing and thawing (ASTM C666 – procedure A) on three different types of Geopolymer concrete studied using three types of pozzolanic material: fly ash, metakaolin and ground granulated blast furnace slag (GGBFS).…
In this study, the effect of rapid freezing and thawing (ASTM C666 – procedure A) on three different types of Geopolymer concrete studied using three types of pozzolanic material: fly ash, metakaolin and ground granulated blast furnace slag (GGBFS). The Geopolymer concrete was prepared using 400 kg of the pozzolanic material with alkaline liquid prepared at 8 molar concentration with normal fine and coarse aggregates. The ratio of alkaline to fly ash and GGBFS was 1.5: 1 and for metakaolin was 2: 1 for workability and compressive strength requirements.
Specimens (100 × 100 × 400) mm were exposed to 100, 200 and 300 cycles of freezing and thawing. The decrease in measured compressive strength was (23, 43, and 26%) for Fly ash, metakaolin and GGBFS respectively. The investigated types of concrete showed good resistance to freezing and thawing. The durability factor of these types was (77%, 68%, and 81%) for fly ash, metakaolin, and GGBFS respectively.